題名 | 以PmIA/PU共聚合體製造高強力/高耐熱性人工皮革之研究 |
---|---|
作者姓名(中文) | 林明芳; 莊富盛; | 書刊名 | 逢甲學報 |
卷期 | 27 1994.11[民83.11] |
頁次 | 頁263-278 |
分類號 | 475.1 |
關鍵詞 | 人工皮革; 共聚合體; 高耐熱性; 高強力; |
語文 | 中文(Chinese) |
中文摘要 | 本實驗及以聚(間-次苯基間苯醯胺)( PmIA )( 商品名Nomex )來改質傳統 的聚氨基甲酸酯( PU )所製成的 PmIA/PU 共聚合體, 使用濕式直接塗佈加工法及含浸加 工法,對 Nylon 6 細丹尼( Id )不織布做加工,以製備人工皮革。 並探討其與傳統聚氨 基甲酸酯( PU )之人工皮革在物性上的差異。 由實驗結果顯示,以自製之 PmIA/PU 共聚 合體樹脂在物性方面均較傳統 PU 人工皮革佳。 |
英文摘要 | In this study, the traditional polyurethane was modified with wholly- rigid aramid poly (mphenylene isophthalamide) (PmIA) and reinforced by copolymerization and then the artificial leather was produced by wet-coagulating and dipping method in which the resin of PmIA/PU was applied to base (Nylon 6 fine dinier nonwoven fabric). Finally, the properties of artificial leather were tested and compared with commercial leather. The experimental consequence showed that the artificial leather of PmIA/PU resin was better than traditional polyurethane. |