查詢結果分析
相關文獻
- Internal Cation Mobilities in the Molten Binary Systems LiCl-AlCl[feb0]and KCl-AlCl[feb0]
- 室溫型熔融鹽電解質磁性薄膜之脈衝電解電鍍
- The Electrodeposition of Molybdenum from Low Temperature Ammonium Formate Molten Salt
- The Electrodeposition of Tungsten in the Low Melting Molten Carbamide Electrolyte
- Fabrication of Platinum Coated Titanium Electrodes from Molten Salt Electrolytes by the Electrodeposition Process
- Transport Property of Cations Li[feb7]and K[feb7]in the Molten Salt Electrolyte
- Electrodeposition of Aluminum in the High Temperature Aluminum Chloride Molten Salt System
- 垃圾資源回收廠工程材料之設計及選用
- 純氧化鋯與鋯砂提煉氧化鋯之結晶構造分析比較研究
- 熔融鹽腐蝕
頁籤選單縮合
題名 | Internal Cation Mobilities in the Molten Binary Systems LiCl-AlCl[feb0]and KCl-AlCl[feb0]=熔融二元系LiCl-AlCl[feb0]及 KCl-AlCl[feb0]之陽離子內部移動度 |
---|---|
作者姓名(中文) | 楊肇政; | 書刊名 | 國立雲林技術學院學報 |
卷期 | 1 1992.06[民81.06] |
頁次 | 頁137-143 |
分類號 | 341.372 |
關鍵詞 | 內部移動度; 熔融鹽; 反電流電泳動; Internal mobility; Molten salt; Countercurrent-electromigration; |
語文 | 英文(English) |
中文摘要 | 不同溫度及濃度條件下,二元系熔融混合物LiCl-AlCl3,KCl-AlCl3之 陽離子內部移動度比率,可利用KlemmColumm方法加以測定。前者之溫度範圍 為408K≦T≦543K,0.757≦XAlCl3 ≦0.890;後者之測定範圍則為483K≦T≦ 603K,0.785≦XAlCl3 ≦0.919。經由實驗所得之Σ12值,及已知之密度與導電 度數據,可以計算出陽離子之內部移動度,bLi或bK及bAl。依結果顯示,各 二元系之陽離子移動度,bAl及bLi或bK的大小,隨著氯化鋁組分之增加而減 少,而鍼金屬陽離子之移動度bM(M:Li,K)則隨均較bAl為大。等溫條件下,bM 值隨著XM增加而增大的趨勢,與熔融二元系鍼金屬─陽離子Al+3與C�籀� 離子間具有較大的作用力,乃為影響離子性融體材料之離子移動度等輸送現象 之主因。 |