題 名 | 無粘結劑鐵粉的溫壓工藝研究=Investigation on Warm Compaction for No-Binder Iron Powders |
---|---|
作 者 | 果世駒; 李明怡; 林濤; 趙燕斌; 李森蓉; 劉廣敏; 張海波; | 書刊名 | 粉末冶金會刊 |
卷 期 | 22:3 1997.08[民86.08] |
頁 次 | 頁224-228 |
分類號 | 454.8 |
關鍵詞 | 無粘結劑鐵粉; 溫壓; 粉末冶金; No-binder iron powder warm compaction powder metallurgy; |
語 文 | 中文(Chinese) |
中文摘要 | 開發了一種無粘結劑武鋼鐵粉的溫壓工藝,其溫壓溫度低於 Ancordense 溫壓工 藝。測定了試樣的生胚密度和燒結密度,擬定了溫壓生胚密度隨壓制壓力的變化曲線,並對 幾種溫壓工藝的效果進行了比較。 |
英文摘要 | Warm compaction process of no-binder iron powder made in Wuhan Iron and Steel Copporation, China has been developed. The green density and sintering density of samples has been measured. The curve of warm-compact green density vs. compact pressure has been described. The results of several warem compaction processes were compared. warm compaction processes were compared. |