題名 | 廢棄物回收再製廢纖板之可行性研究=Feasibility of Junk Fiber Plank Regenerated Using the Recycled Waste Material of Industry |
---|---|
作者姓名(中文) | 李文仁; 李貴琪; | 書刊名 | 華岡紡織期刊 |
卷期 | 4:3 1997.09[民86.09] |
頁次 | 頁233-241 |
分類號 | 478.1 |
關鍵詞 | 廢纖維; 聚丙烯; 混棉; 梳棉; 熱壓; Waste fabric; Polypropylene; Mixed fibre; Carding; Hot press; |
語文 | 中文(Chinese) |
中文摘要 | 本研究係採廢纖維為強化材,以熱可塑性聚丙烯纖維為基材,依強化材和基材之重量百分比70:30,經由開混棉、梳棉及熱壓等工程製成廢纖板,藉著改變成形條件,來探討複合材之合浸效果、機械性質及其最佳成形條件。由實驗結果得知其最佳成形時間4min、成形壓力40kgf/cm□、成形溫度200℃。 |
英文摘要 | The thermoplastic polypropylene was used as the matrix mixing and carding waste fiber m this study. The weight percentage ratio of combination of the reinforced material and matrix is 70:30. The waste fiber wood was used to form the mixing, carding and hot press sample. The immersion effect, their mechanical properties and the best treatment conditions of the thermoplastic composite material were studied. The results indicate that the best treatment conditions of 10 minutes 40kgf/cm□ and 200℃ can be found. |