題 名 | 磷酸結合包埋材的晶相轉變=Phase Transformation of Phosphate-Bonded Investment |
---|---|
作 者 | 張豐城; 陳麗妃; 黃明發; 楊惠雯; 徐啟智; 呂毓修; | 書刊名 | 中華牙醫學雜誌 |
卷 期 | 17:4 1998.12[民87.12] |
頁 次 | 頁253-261 |
分類號 | 416.98 |
關鍵詞 | 磷酸結合包埋材; X光粉末繞射; Phosphate-bonded investment; X-ray powder diffraction; |
語 文 | 中文(Chinese) |
中文摘要 | 本研究的目的乃利用X光粉末繞射(X-ray powder diffraction,XRD)分析磷酸結 合包埋材加水及加專用液的硬化及熱化學反應,並與 Neiman 研究的包埋材反應機構作比較 討論。磷酸結合包埋材主要含耐火的填料及黏結劑。包埋材的硬化及熱化學反應以黏結劑的 反應為主。 黏結劑與水初期硬化反應生成物為含 6 個水的磷酸鎂氫氨 (NH �� MgPOh ��, . 6H �� O); 而與專用液初期硬化生成物為含有磷酸矽 (SiP �� O �f, )。 兩者在 200-500 ℃時,非結晶性玻璃性聚合物 (MgP �� O �f )n 為中間生成物。 而在 1000 ℃時 ,兩者的最後生成物為焦磷酸鎂 (MgP �� O �f ) 存在於填料石英及白矽土中。本研究利用 XRD 分析磷酸結合包埋材的加水硬化熱化學反應與 Neiman 的反應機構相符合,而加專用液 乃改良 Neiman 的初期硬化反應機構。 |
英文摘要 | The purpose of this project was to study the thermal phase reactions of phosphatebonded investments blended in water or in a specific Shofu investment liquid. The results were in accordance with Neiman's reaction mechanism of phosphate-bonded investment. The major components of a phosphate-bonded investment are fillers and binders. The thermal phase reactions of the investment depend upon the binder's reactions. The initial hardening reaction product of binder with HgO �� was NH �� MgPO �瓷D 6H �� O while the binders with the specific Shofu investment liquid was SiP �� O �f. Between 200-500 ℃, these setting products became an intermediate product (NH �� MgPO �� )n, an amorphous glassy polymer. After firing to 1000 ℃, the major phases of phosphate-bonded investments with water or specific Shofu investment liquid were MgP �� O �f, α -quartz and cristobalite. Our research results showed that the thermal phase reactions of phosphatebonded investments with water agreed with Neiman's mechanisms from XRD analyses. |