查詢結果分析
相關文獻
- 速生樹種之理化學性質及膠合方法對集成材性能之影響(12):臺灣二葉松、桃花心木、柚木縱向接合製作集成材之研究
- 速生樹種之理化學性質及膠合方法對集成材性能之影響(11):臺灣二葉松、桃花心木、柚木製作集成材之研究
- 速生樹種之理化學性質及膠合方法對集成材性能之影響(10):臺灣二葉松、桃花心木、柚木之基本理化學性質
- 速生樹種之理化學性質及膠合方法對集成材性能之影響(9):相思樹、楓香、臺灣杉縱向接合製作集成材之研究
- 速生樹種之理化學性質及膠合方法對集成材性能之影響(6):柳杉、臺灣泡桐、木油桐縱向接合製作集成材之研究
- 速生樹種之理化學性質及膠合方法對集成材性能之影響(5):柳杉、臺灣泡桐、木油桐製作集成材之研究
- 速生樹種之理化學性質及膠合方法對集成材性能之影響(7):相思樹、楓香、臺灣杉之基本理化學性質
- 速生樹種之理化學性質及膠合方法對集成材性能之影響(II):杉木、山黃麻、摩鹿甲合歡製作集成材之研究
- 速生樹種之理化學性質及膠合方法對集成材性能之影響(I):杉木、山黃麻、麻六甲合歡之基本理化學性質
- 速生樹種之理化學性質及膠合方法對集成材性能之影響(8):相思樹、楓香、臺灣杉製作集成材之研究
頁籤選單縮合
題名 | 速生樹種之理化學性質及膠合方法對集成材性能之影響(12):臺灣二葉松、桃花心木、柚木縱向接合製作集成材之研究 |
---|---|
作者姓名(中文) | 李文昭; 劉正字; | 書刊名 | 林產工業 |
卷期 | 10:1 1991.03[民80.03] |
頁次 | 頁25-34 |
分類號 | 436.18 |
關鍵詞 | 性能; 柚木; 桃花心木; 理化學性質; 速生樹種; 集成材; 臺灣二葉松; 膠合; 縱向接合; |
語文 | 中文(Chinese) |
中文摘要 | 本研究以台灣二葉松、桃花心木、柚木為試材,尿素膠為膠合劑,探討其經由各種不同對接、斜接、指接等端部接合斷面及接口排列位置所製作之四層集成材之性質,所得結論如下:1.對接膠合集成材隨各層接口位置錯開之間距加大,其強度增加;而底層改用完整集成元者,其強度顯著改良而與四層均用完整集成元所製作者強度相近。2.斜接膠合集成材隨斜角長度(L/H)及各層接口間距加大,其強度增加;且底層改用完整集成元者其強度亦明顯增加。3.指接膠合者其靜曲強度略低於L/H為8.0之斜接膠合者,且將各層接口位置錯開時其對強度之改良效果並不顯著。 |
英文摘要 | The purpose of this study was to investigate the properties of 4-plies laminated wood made from Taiwan red pine , Honduras mahogany and common teak with butt, scarf and finger joint by UF adhesive, and with different location of joint in laminated wood. The results obtained were as follows: 1. The strength of butt joint laminated wood could be improved when the distance between each butt joint increased, when use the full-length lamina as bottom lamina in laminated wood, its strength would be improved significantly and up to the strength of laminated wood made from four full-length laminas. 2. The strength of scarf joint laminated wood could be improved as increasing either the ratio of horizontal length (L) to vertical length (H) of the slope or the distance between each scarf joint. The over all strength could be improved obviously when use the full-length lamina as bottom lamina in scarf joint laminated wood. 3. The bending strength of finger joint laminated wood was slightly lower than the scarf joint laminated wood with L/H ratio of 8.0. The strength of finger joint laminated wood had a little or no progress as the finger joint position in each lamina was not on a line. |