| 題 名 | 鋼材滲鋅法之研究 |
|---|---|
| 作 者 | 杜讚發; | 書刊名 | 技術學刊 |
| 卷 期 | 1:1 1986.09[民75.09] |
| 頁 次 | 頁71-78 |
| 分類號 | 472.3 |
| 關鍵詞 | 滲鋅法; 鋼材; |
| 語 文 | 中文(Chinese) |
| 中文摘要 | 本文主要探討S45C鋼材之滲鋅處理,我們以200網目92.5% Zn,5% SiO₂, 2.5 % Al₂ O₃ ,作為滲鋅劑。在360-410℃之溫度範圍,對鋼材作1 -8小時之滲鋅處理。我們將對下列項目作廣泛性之研討。 1. 滲透層厚度與滲透溫度及時間之關係。 2. 滲透層之耐蝕性。 3. 滲鋅零件之機械性質。 |
| 英文摘要 | Sherardization of S45C steel was studied in the present research. The mixture of 92.5 Zn (200 mesh) + 5 SiO₂ + 2.5 Al₂O₃ by weight was used as our sheradizer. The diffusionzinc coating was done at temperatures of 360 - 410 deg C for 1-8 hours. The following points were addressed; 1. the relationship of the thickness of the diffusion layer, the temperature and the time. 2. the corrosion resistance of the sherardized layer. 3. the mechanical properties of the sherardized parts. |