查詢結果分析
相關文獻
- 影響鐵奈米材料之粒徑大小分佈及其穩定性之因子探討
- 固體邊界效應對多孔性介質中自然對流不穩定性之影響
- 界面活性劑葡聚醣披覆四氧化三鐵磁性奈米粒子之製備及其特性之研究
- 四氧化三鐵磁性奈米粒子之製備與特性研究及其在腫瘤熱治療之應用
- Production Control and Characterization of Bilayer-Surfactant Coated Stable Water-Soluble Monodisperse Magnetic Iron Oxide Nanoparticle
- 林肯大郡災變後建築物結構安全度之探討
- 以林肯大郡為例談坡地開發之地工問題
- Study of Marangoni Instability of an Evaporating Liquid Layer
- Dry Deposition and Particle Size Distribution of PAHs in Both Petrochemical-industry and Urban Areas
- Influence of Lubricant on Limit Drawing Ratio in Cup-Drawing Process: A Stabilization Matrices Scheme
頁籤選單縮合
題名 | 影響鐵奈米材料之粒徑大小分佈及其穩定性之因子探討=Study on the Influence Factors of Particle Size Distribution and Stability of Fe₃O₄ Magnetic Nanoparticles |
---|---|
作者 | 蔡長書; 徐維駿; 戴國峯; | 書刊名 | 慈濟科技大學學報 |
卷期 | 1=25 2015.09[民104.09] |
頁次 | 頁85-107 |
分類號 | 410.1644 |
關鍵詞 | 磁性奈米粒子; 葡聚醣; 粒徑分佈; 穩定性; Magnetic nanoparticles; Dextran; Particle size distribution; Stability; |
語文 | 中文(Chinese) |
中文摘要 | 四氧化三鐵(Fe_3O_4)磁性奈米粒子具有超順磁性、高飽和磁化量及高有效表面積等特性,披覆葡聚醣界面活性劑,以修飾其團聚特性及生物相容性等問題,目前已廣泛的被運用在生物醫學的研究與應用領域上,例如,腫瘤治療、靶向藥劑、基因篩選或細胞分離、核磁影像檢測等。由於粒徑大小分佈和穩定性會影響到磁性奈米粒子作為生醫材料的體外可用性,以及體內生物相容性、細胞毒性及載體作用等。本研究旨在探討其粒徑大小分佈及影響其穩定性之因子。包含反應莫耳濃度、反應溫度、pH 值、粒子型態及粒徑分佈與製備後樣品保存時間及不同溫度環境等參數之探討。結果發現在高溫90℃±5℃;pH 值為10-12;反應時間2 小時可產生出純度佳的Fe_3O_4,披覆葡聚醣條件反應溫度80℃±5℃;反應時間2 小時為最適化條件;四氧化三鐵磁性奈米鐵粒子保存在4℃、22℃、37℃、43℃及47℃溫度下2 天內,可獲得良好的超順磁性且粒徑大小穩定、分佈均勻。粒徑大小介於123.5±25.56 nm的範圍。披覆葡聚醣界面活性劑(one-step process)在4℃、22℃、37℃、43℃及47℃範圍7 天內皆有很好穩定性 , 粒徑大小界於135.3±25.06nm 的範圍。披覆葡聚醣界面活性劑(two-step process) 在4℃、22℃、37℃約 5 天內皆有很好穩定性 , 粒徑大小界於156.6±24.13 nm 的範圍,於第3 天後可發現逐漸產生不穩定團聚現象,七天內大幅團聚增至約210nm 大小。 |
英文摘要 | Fe_3O_4 magnetic nanoparticles (MN) were prepared by using chemical co-precipitation method and were coated with reduced dextran which can modify MN with biocompatibility and stability. Furthermore, to ensure desirable qualities, all MN compounds obtained in this study were examined by superconducting quantum interference device, X-ray diffraction, fourier transform infrared spectroscopy, ultraviolet-visible spectroscopy, scanning electron microscope and energy-dispersive X-Ray Spectroscopy. We found that Fe_3O_4 MN with high purity could be obtained with the following reaction condition: 90°C ± 5°C; pH value of 10-12; 2 hours reaction time. On the other hand, one-step and two-step synthesis pathways were used to coat Fe3O4 MN with reduced dextran with the reaction temperature of 80°C ± 5°C and 2 hours reaction time. The data of size distribution of MN shows its characteristics and stabilities can be maintained for 2 days at 4°C, 22°C, 37°C, 43°C and 47°C, respectively. The average size of such MN is ca. 123.5 ± 25.56 nm; The dextran@MN derived from one-step synthesis pathway is able to hold stabilities and non-agglomeration for 7 days at 4°C, 22°C, 37°C, 43°C and 47°C, respectively. The average size of the above dextran@MN is ca. 135.3 ± 25.06 nm; Although the dextran@MN by two-step synthesis pathway retained stabilities and good characteristics for 5 days at 4°C, 22°C and 37°C, respectively, it started to aggregate at the third day post synthesis and the sizes grown to over 210 nm at the seventh day. The average size of such dextran@MN by two-step method is ca. 135.3 ± 25.06 nm. |