題 名 | 添加三種塑化劑於混煉玉米澱粉塑膠粒中對其熱特性及生物分解性之影響=The Effects of Adding Three Plasticizers in Cornstarch Plastic Pellets on Their Thermal Properties and Biodegradability |
---|---|
作 者 | 李柏廷; 吳佳洋; 彭錦樵; | 書刊名 | 台灣農學會報 |
卷 期 | 14:1 2013.02[民102.02] |
頁 次 | 頁1-16 |
分類號 | 467.4 |
關鍵詞 | 熱特性; 生物分解性; 塑化劑; Thermal properties; Biodegradable; Plasticizer; |
語 文 | 中文(Chinese) |
中文摘要 | 本研究探討添加三種塑化劑以擠壓加工技術配合反應曲面法之實驗設計開 發生物可分解塑膠原料粒,並對生產出的塑膠粒進行熱特性與生物分解性之測 試,並建立其迴歸模式。擠壓機操作條件之設定為螺軸轉速 40rpm、套筒三段溫 度分別控制為 170℃、170℃與 175℃,模具溫度設為 175℃及進料速率 20 g/min。研究原料配方 ( 總重 1Kg) 對熱特性做分析及評估,由結果可知,樣品 熔點 Tm 值大約在 154.2 ~ 160.1℃之間,而樣品熱裂解溫度 Td 值大約在 248.2 ~ 276.6℃之間。此外,本研究依照 CNS 14432 之規定進行生物分解度 測定,發現樣本於第 35 天生物分解度已達 70.6%,而第 45 天時達 79.5%, 均已超過我國國家標準 CNS 14432 規定之 70%,故判定本研究所研發之生物可 分解塑膠原料之最適化產品具生物可分解性。本研究結果應可做為進一步研究及 商品化之參考,並期能協助解決日益嚴重的環境問題。 |
英文摘要 | In this study, response surface methodology (RSM) was used to analyze the effect of glycerol, triethyl citrate (TEC) and dioctyl sebacate (DOS) on the thermal properties of biodegradable pellets as well as the biodegradability attributes of a polyhydroxybutyrate-co-valerate (PHBV) /corn starch-blended plastic resin. The experiments (total weight of 1 kg) were run at barrel temperatures of 170 ℃ , 170 ℃ , 175 ℃ , and a die temperature of 175 ℃ , respectively, with a screw speed of 40 rpm and a feed rate of 20 g/min. The result indicated that the melting points (Tm) of extruded pellets ranged from 154.20℃~ 160.10℃ and the thermal degradation temperatures (Td) ranged from 248.16℃~ 276.59℃ . The biodegradability of the extruded pellets was tested according to the CNS14432 standard. The result indicated that the biodegradability of the extruded pellets reached 70.6% after 35 days and 79.50% after 45 days, respectively. Therefore, it could be concluded that the plastic pellets developed in this study consist of biodegradable properties, which can help to solve environmental problems. These pellets are suitable for industrial application. |