頁籤選單縮合
題名 | 以田口法優化大量微細銅粉合成參數之研究=A Mass Production Method for Synthesizing Ultrafine Copper Powder Optimized Using the Taguchi Method |
---|---|
作者 | 彭御賢; 楊志豪; 李清華; 陳冠廷; 湯柏炘; | 書刊名 | 科學與工程技術期刊 |
卷期 | 7:3 2011.09[民100.09] |
頁次 | 頁1-11 |
分類號 | 460.02 |
關鍵詞 | 化學還原; 田口式優化試驗法; 微細銅粉; Chemical reduction method; Taguchi robust design method; Ultrafine copper powder; |
語文 | 中文(Chinese) |
中文摘要 | 本研究主要探討於液相中以化學還原方式搭配田口式優化試驗法進行實驗設計,並針對不 同還原劑種類(因子A)、反應溫度(因子B)、還原劑劑量(因子C)與反應器轉速(因子 D)等參數,針對銅粉生成之轉換率、粒徑大小、反應時間所產生之影響進行探討,其中還原 劑種類與反應溫度於本研究之反應體系中乃是相對影響最顯著之因子。本研究最終所得到之最 佳操作參數為以次亞磷酸鈉作為還原劑、反應溫度控制在70°C、還原劑添加量8.14 kg、反應 器轉速300 RPM;將合成之微細銅粉經由感應偶合電漿發射光譜儀(ICP-OES)、雷射粒徑分 析儀(DLS)、掃描式電子顯微鏡(SEM)與X 射線晶體分析儀(XRD)等儀器分析後,證明 可得到一具有面心立方(face-centered cubic, FCC)純銅粉結構、不純物含量低於0.06%、D50 粒徑為1.51 μm 之高純度微細銅粉,此法不僅沒有添加任何表面活性劑,且製程簡易適合工廠 規模大量生產。 |
英文摘要 | The Taguchi robust design method was used to optimize the experimental conditions for the synthesis of ultrafine copper powder via a chemical reduction method. The reducing agents, reactiontemperatures, weight-reducing agents, and stirring rates were chosen as the primary factors, while the conversion rates, particle sizes, and reaction times were selected as the desired targets. The results indicate that the reducing agent and the reaction temperature were comparatively the significant factors affecting the desired targets. The optimum conditions were as follows: factor A (reducing agent) at level 2 (NaH2PO2•H2O), factor B (temperature) at level 3 (70°C), factor C (weight-reducing agent) at level 3 (8.14 kg), and factor D (stirring rate) at level 2 (300 RPM). The results of the experimental confirmations for the three desired targets were matched with the predictions of the Taguchi method. Additionally, via an inductively coupled plasma emission spectrometer (ICP-OES), laser particle size analyzer (DLS), scanning electron microscopy (SEM), and X-ray diffraction (XRD) analyses, the pure (impurity <0.06 %) face-centered cubic structure with 1.51 μm medium size of the HUCP1 was characterized and determined. Finally, a surfactant-free facility and a method suitable for mass production were established to synthesize high-purity ultrafine copper powder. |
本系統之摘要資訊系依該期刊論文摘要之資訊為主。