查詢結果分析
相關文獻
- Kinetics of Hydrogen Oxidation Reaction on Nafion-coated Pt/C Electrodes under High Overpotentials
- A Kinetic Study on the Kolbe Electrolysis of Methyl Hydrogen Adipate Using a Rotating Disk Electrode
- Characterization of Fuel Cell Catalysts by Cyclic Voltammetry and Rotated Disk Voltammetry
- Uterine Myoma after Cessation of Gonadotropin-Releasing Hormone Agonist: Ultrasound and Histopathologic Findings
- 以聚苯乙烯和含羥基之苯乙烯共聚物為共膜材料製備乙基纖維素微膠囊及其制放行為研究
- Cloning of Mercury Resistance Determinants in Escherichia coli and Analysis of Mercury Reduction Activity in vivo and in vitro
- 選擇性血清素再吸收抑制劑
- Fluvoxamine對Clozapine藥物動力學之影響
- GPS精密軌道與軌道預估之計算研究
- 踝關節運動力學之幾何特性
頁籤選單縮合
題名 | Kinetics of Hydrogen Oxidation Reaction on Nafion-coated Pt/C Electrodes under High Overpotentials=Nafion覆蓋Pt/C電極在高過電位下氫氣氧化反應的動力學 |
---|---|
作者姓名(中文) | 林仁斌; 施信民; | 書刊名 | Journal of the Chinese Institute of Chemical Engineers |
卷期 | 38:5/6 2007.09-11[民96.09-11] |
頁次 | 頁365-370 |
分類號 | 460.02 |
關鍵詞 | 氫氣氧化反應; 動力學; 旋轉電極; Platinum on carbon; Nafion; Rotating disk electrode; Hydrogen oxidation; Fuel cells; |
語文 | 英文(English) |
中文摘要 | 本研究以旋轉電極探討浸沒在0.5M硫酸液中的Nafion覆蓋20wt% Pt/C電極之Nafion膜厚與鉑黑負載量對氫氣氧化反應動力學的影響。Nafion膜的厚度(≦8μm)對表面積量測幾無影響。在高過電位 (0.4V)下所估算的動力學參數因鞽數據處理方法以而有所不同。Nafion膜厚度小於0.2μm時,膜內的氫氣質傳阻力可以忽略。氫氣在Nafion 膜中的滲透係數介於2.4×10^(-5)~4.8×10^(-5) mM cm²/s之間。誤差分析顯示所估算的視動力電流是由於實驗誤差所致,而非如先前研究者所提出是由於化學程式所致。 |
英文摘要 | The influences of the Nafion film thickness and Pt loading on the kinetics of the hydrogen oxidation reaction on Nation-Coated 20 wt% Pt/C electrodes immersed in 0.5 M H₂SO₄ were investigated using a rotating disk electrode configuration. The coating of a Nafion film (≦8μm) had a negligible effect on the electrochemical surface area of an electrode. The kinetic parameters were estimated at an overpotential of 0.4V; the values obtained were shown to vary with the method of data treatment. The diffusional resistance for H2 in the Nafion film was negligible when the film was thinner than 0.2μm. The permeability of H₂ in the Nafion film ranged from 2.4×10^(-5) to 4.8×10^(-5)mM cm²/s. The error analysis demonstrated that the apparent kinetic current estimated was resulted from experimental errors, instead of resulting from a chemical process as proposed by some previous investigators. |