查詢結果分析
相關文獻
- Kinetic and Interfacial Characterization of Lithium Electrodes in Organic Electrolyte Solutions
- 以頻譜分析估計地下水非受壓含水層水力擴散係數
- Hydrogen Trapping Ability of Steels with Different Microstructures
- The Kinetics of the Dyeing of Azo Thiazole Disperse Dyes on Polyester Fabric
- 應用頻譜分析反求解地下水水力擴散係數之不確定性與參數敏感度分析
- 應用脈衝式核磁共振量測醣類水溶液及果汁之可溶性固形物含量
- 應用簡單最佳化法輔助平面熱源法同時量測熱傳導係數、熱容量及熱擴散係數
- 射出厚件陶瓷之溶劑脫脂行為
- Assessment of Chlorde Diffusion in High Strength Concrete Using the Accelerated Ionic Migration
- 臺南與高屏沿岸表層流況及水平擴散之觀測
頁籤選單縮合
題 名 | Kinetic and Interfacial Characterization of Lithium Electrodes in Organic Electrolyte Solutions=鋰電極在有機電解質溶液中的電極動力及界面特性表徵 |
---|---|
作 者 | 張裕祺; 鍾志華; 費定國; | 書刊名 | Journal of the Chinese Institute of Chemical Engineers |
卷 期 | 35:4 2004.07[民93.07] |
頁 次 | 頁425-433 |
分類號 | 341.372 |
關鍵詞 | 鋰電極; 有機電解質溶液; 電極動力; 擴散係數; 化學沉積; Lithium electrode; Organic electrolytes; Kinetics; Electrode capacitance; Diffusivity; |
語 文 | 英文(English) |
中文摘要 | 本研究以電流脈動法及定電荷階躍法測求鋰電極在若干重要的鋰二次電池有機電解質溶液中的動力學參數,如極化電阻,交換流密度及電荷轉移係數。所探討的溶液系統為EC-DEC混合溶劑及PC溶劑與相應LiPF₆、LiClO₄、LiBF₄等電解質之組合。另外亦測求界面電容值。就1M LiClO₄/PC及1M LiPF₆/EC-DEC(1:1)的量測結果言,所測得之值與文獻所載相近。研究結果顯示鋰在1M LiPF₆/EC-DEC溶液中的極化電阻隨浸放時間變化甚緩,但在1M LiPF₆/PC溶液中則增加甚速。又界面電容則在各溶液中皆隨浸放時間延長降低。本研究亦以微圓盤電極探究鋰在1M LiPF₆/PC-DEC溶液中的電化學沉積及溶解程序,並測求擴散係數。 |
英文摘要 | Kinetic parameters, such as polarization resistance, exchange current density, and transfer coefficient, for lithium electrodes in a few important lithium battery electrolyte solutions were determined at 27℃ using the galvanostatic pulse technique and constant charge-step method. The solvents used were ethylene and diethyl carbonates mixtures and propylene carbonate. The electrolytes used were LiPF₆, LiClO₄, and LiBF₄. The electrode capacitance was also measured. The effects of the electrolyte concentration and storage time on the polarization resistance and the electrode capacitance were examined. The data obtained for lithium in 1 M LiClO₄/PC and 1 M LiPF₆/EC-DEC(1:1) electrolyte solutions are consistent with those reported in the literature. During two days of storage, the polarization resistance of the lithium in the 1 M LiPF₆/EC-DEC solutions only increased slightly, but the polarization resistance of the lithium in the 1 M LiPF₆/PC solutions increased remarkably. The electrode capacitance, however, decreased during prolonged storage for the systems studied. A nickel microdisk electrode was also used to study the electrodeposition and electrodissolution of lithium in the 1 M LiPF₆/EC-DEC (1:1) electrolyte solutions. The diffusion coefficient was also determined. |