查詢結果分析
相關文獻
- 木材表面緻密化之研究
- Mechanical Characteristics of Self-lubricating Aluminum/SiC/Nickel-coated-graphite Composite Synthesized by Semi-solid Powder-densification Method
- Sintering Behavior and Microstructure of Nano-Mo/Al[feaf]O[feb0] Composites
- 粉末體熱壓快速緻密化研究
- 提高鐵粉燒結密度之方法
- 粉末半固態成型之鋁/碳化矽/鍍鎳石墨複合材料磨潤行為
- 高承載鋁基複合材料製程及界面熱傳導性質研究
- 添加Cr元素對θ-Al[feaf]O[feb0]微粉末燒結的影響
- 燒結理論
- The Effects of Sintering Time and Temperature on the Densification and Phase Evolution of Mullite-30 Vol%(3 Mol%Yttria-Zirconia)
頁籤選單縮合
題名 | 木材表面緻密化之研究=Study on Densification of Wood Surface Layer |
---|---|
作者 | 許妙戎; 陳載永; 陳合進; 徐俊雄; | 書刊名 | 林業研究季刊 |
卷期 | 22:4 2000.12[民89.12] |
頁次 | 頁1-11 |
分類號 | 436.18 |
關鍵詞 | 木材表面; 緻密化; 密度剖面; Wood surface; Densification; Density profile; |
語文 | 中文(Chinese) |
中文摘要 | 密度木材及疏伐木之利用價值,以臺灣杉(Taiwan cryptomerioides)、杉木(Cunninghamia lanceolata)小徑木為試材,分別經浸水-熱壓、浸水-冷凍-熱壓及浸水-蒸煮-熱壓之處理後,形成表度較中間層密度為高之材料,然後分別檢測材料的密度剖面、吸水率、吸水厚度膨脹率、靜曲強度、硬度與壓縮強度等性質。未處理之試材平均含水率約為12±2%,經各條件處理後之試材含水率均約為2±1%。處理過之試材置於室溫下,其尺寸極為安定,回彈約0.5-0.7%。浸水-熱壓與浸水-冷凍-熱壓處理者其吸水厚度膨脹率隨吸水率增加而增加,而浸水-蒸煮-熱壓處理者則無。三種處理方法均能提升表面密度,達表面緻密之效果,其中以浸水-冷凍-熱壓處理者效果最明顯,其表面密度平均可達2g/cm3以上,遠高於中間層的密度(0.43g/cm3)。處理後試材之表面粗糙度較對照組試材鉋光者低,即經處理之試材表面較光渦。浸水-熱壓及浸水-冷凍-熱壓兩種處理提高靜曲強度30~130%、硬度8 ~86%及壓縮強度25~70%,具有明顯之改善效應,而浸水-蒸煮-熱壓處理者僅對壓縮強度具有改善效應,但浸水-蒸煮-熱壓處理對表面緻密化的臺灣杉之靜曲強度產生負效應,約降低30%。 |
英文摘要 | To improve the quality and performance of low-density wood and thinning logs, Taiwania(Taiwania cryptomerioides) and China fir (Cunninghamia lanceolata) were treated by soaking, soaking freezing and soaking-cooking in water respectively, and then hot-pressed (20°C). The density of surface layer is higher than that of middle layer after treatments. The physical properties (such as density profiles, water absorption and thickness swelling) and mechanical properties (such as static bending strength, hardness, compressive strength parallel to grain) of the treated materials were tested. The average moisture content of untreated materials to 12±2%, and that of treated materials approximates to 2±1% only. The spring-back of treated materials (0.5-0.7%) is not obvious. The thickness swelling of treated materials that were soaked in water and frozen increased with water absorption increased, but cooking treatment were not. The densification of surface layer would be increased by soaked, frozen and cooked in water respectively. The density of surface layer by frozen treated (2g/cm3) is higher than that of middle layer (0.43g/cm3). The surface roughness of treated materials was lower than untreated ones. It showed more smooth on the surface of treated materials. The dimension stability of treated materials was stable under room temperature. The static bending strength, hardness and compressive strength parallel to grain would be obviously enhanced by soaked in water and frozen treated, but treated with cooked ones were not except for comprerssive strength. The MOE of cooking treated Taiwania decrease about 30%, but the others show positive effects in 30~130% enhanced obviously. |