題 名 | 銲接熱裂縫之理論及機制=The Principle and Mechanism of Hot Cracking in Welding |
---|---|
作 者 | 江家慶; 王星豪; | 書刊名 | 銲接與切割 |
卷 期 | 10:2 2000.03[民89.03] |
頁 次 | 頁41-51 |
分類號 | 472.14 |
關鍵詞 | 銲接; 熱裂縫; |
語 文 | 中文(Chinese) |
中文摘要 | 銲接已成為工業及工程中不可或缺的一環,然隨著不�袟鶠B耐高溫合金、高合金 鋼、超合金、甚至非鐵合金... 等特殊材料之運用日益廣泛,在銲接過程中這類材料常有熱 裂縫的情形發生,因此藉由了解裂縫產生的機構進而去防制其形成乃當務之急,本文將對熱 裂縫之發生的原理作一番討論。 |
英文摘要 | Welding bas been one of the most important parts of fabrication in the industry and the engineering. As stainless steels, high temperature resistance of alloy steels, high alloy steels, supperalloys and even nonferrous alloys...etc., are widely used, hot cracking often occurs during the welding process in these materials. Therefore, it is important to understand the theory and mechanism of the hot cracking so as to prevent welds from cracking. This report will discuss the foundamedtal of the occurrence of hot cracking. |