題名 | CMC對於漿膜物性之影響=The Effect of CMC on the Mechanical Properties of Size Films |
---|---|
作者 | 秦秀香; 施陽平; 魏亞中; Chyn, S. S.; Shih, Y. P.; Wei, Y. C.; |
期刊 | 紡織中心期刊 |
出版日期 | 19980100 |
卷期 | 8:1 1998.01[民87.01] |
頁次 | 頁58-64 |
分類號 | 478.1 |
語文 | chi |
關鍵詞 | 溼度; 相容性; 羧甲基纖維素; Humidity; Miscibility; Carboxymethyl cellulose; |
中文摘要 | 本文探討CMC對於漿膜物性之影響,在聚乙烯醇與化工澱粉漿料中添加不同比例的CMC,調製成漿膜於71%RH 及 85%RH溼度測試其物性。發現無論完全鹼化PVA或部分鹼化PVA之漿膜以添加3%CMC 得到最佳之強伸度,這項研究結果可提供漿紗現場在調煮漿液時添加CMC量之參考依據。 |
英文摘要 | The effect of CMC on the mechanical properties of size films was studied. CMC was added into the size mixture of polyvinyl alcohol and modified starch. The size solutions were used to prepare the size films which mechanical properties were measured at the condition of 71 %RH and 85%RH. The experimental result indicated that 3% was the optimum content of CMC in PVA/MS mixture. |