題 名 | 中間相瀝青系碳纖維之研究=The Study of the Mesophase Pitch-Based Carbon Fiber |
---|---|
作 者 | 葉淑貞; | 書刊名 | 紡織中心期刊 |
卷 期 | 7:4 1997.07[民86.07] |
頁 次 | 頁286-291 |
分類號 | 478.8 |
關鍵詞 | 中間相瀝青; 碳纖維; Mesophase pitch; Carbon fiber; |
語 文 | 中文(Chinese) |
中文摘要 | 本文係以A240石油瀝青為原料,進行中間相(Mesophase)瀝青紡絲、穩定化、碳化成碳纖維之熱處理效應研究。結果顯示在3℃/min升溫速率下,390℃熱處理溫度可製出具有較佳可紡性的中間相瀝青。 |
英文摘要 | The study was researched with various temperatures and times on the mesophase pitch processes to develop carbon fiber with the A240 petroleum pitch. The results show that the temperature of the heat treatment at 390°C by 3℃/min velocity was better to prepare the spinable mesophase. |