查詢結果分析
來源資料
相關文獻
- 經電化學陽極處理後之鈦金屬表面所引發凝血性質變化之探討
- 二氧化鈦奈米管之管徑與銀擔載量對於其在0.5M硫酸中氧還原催化活性之影響
- Effects of Thrombin on the Growth, Protein Synthesis, Attachment, Clustering and Alkaline Phosphatase Activity of Cultured Human Periodontal Ligament Fibroblasts
- 電腦模擬在鈦合金四面精鍛製程設計之應用
- Hydrophobic Effect of PTFE-Modified Ru矴Ti盁O[feaf]Electrodes on Oxygen Evolution in Alkaline Solution
- Determination of Rate Constants of the Reaction between Titanium Pellet and Nitrogen
- 防曬劑中超微細固態氧化物添加劑其光化學反應機制對防曬功能利弊之探討
- 四氯化鈦在異丙基碳酸酯、異丙醇中電合成鈦金屬粉末
- 物理蒸鍍單層及複層氮化鈦中碳鋼之拉伸及疲勞性質
- 氫氧基磷灰石/鈦磁控濺鍍膜微結構及性質研究
頁籤選單縮合
題 名 | 經電化學陽極處理後之鈦金屬表面所引發凝血性質變化之探討=Titanium Surface Blood Coagulation Changes Induced by Electrochemical Anodization Treatment |
---|---|
作 者 | 陳靜宜; 陳智華; 李天翊; 楊明鈴; 李慈心; 劉嘉民; 黃何雄; | 書刊名 | 防蝕工程 |
卷 期 | 22:1 2008.03[民97.03] |
頁 次 | 頁51-57 |
分類號 | 440.35 |
關鍵詞 | 鈦; 電化學陽極處理; 網狀結構; 凝血; Titanium; Electrochemical anodization; Network structure; Blood coagulation; |
語 文 | 中文(Chinese) |
中文摘要 | 本研究是評估鈦金屬表面經電化學陽極處理後凝血性質的變化。牙科用純鈦表面利用電化學陽極處理製備孔洞狀的鈦-氧層,並以凝血測試及血小板貼附來評估其凝血性質。電化學處理結果顯示,經電化學陽極處理後的鈦表面有二氧化鈦的網狀結構生成。凝血測試結果顯示,經電化學陽極處理的鈦試片比未經處理的鈦試片有較短的凝血時間。血小板貼附觀察結果顯示,經電化學陽極處理後的鈦試片有較多的血小板貼附、活化及聚集的現象。牙科用鈦植體材料表面經由電化學陽極處理可產生網狀的二氧化鈦結構,此結構可增進材料的凝血特性。 |
英文摘要 | This study was to evaluate the blood coagulation changes of commercially pure Ti surface after an electrochemical anodization treatment. Anodization treatment was used to produce a porous Ti-O layer on ground Ti surface for dental implant application. The blood coagulation of surface modified Ti specimens was analyzed using kinetic clotting time method and platelet adhesion observation. Results showed that a network TiO2 layer was developed on Ti surface after anodization treatment. The clotting time of surface modified Ti specimens was shorter than that of the untreated Ti specimen. Surface modified Ti specimens had better platelet adhesion, activation and aggregation. According to the present results, we may conclude that the blood coagulation of Ti surface can be improved using an electrochemical anodization treatment via the formation of a network-structured TiO2 surface layer. |