題名 | Particle Erosion Behavior of SUS403 Tempered Martensitic Stainless Steel=SUS403回火麻田散鐵不銹鋼的沖蝕磨耗 |
---|---|
作者姓名(中文) | 溫東成; 吳朝麟; | 書刊名 | 中華技術學院學報 |
卷期 | 33 民94.12 |
頁次 | 頁41-54 |
分類號 | 472.3 |
關鍵詞 | 沖蝕; 麻田散鐵不銹鋼; 回火; 二次硬化; Particle erosion; Martensitic stainless steel; Impact angle; Hardness; Tempering; Secondary hardening; |
語文 | 英文(English) |
中文摘要 | 本文探討AISI403麻田散鐵不銹鋼經200~600℃回火處理後的沖蝕磨耗,分別討論沖蝕角度與硬度對沖蝕速率和沖蝕機構的影響。結果顯示,低角度沖蝕以長條狀切削凹坑為主,高角度時為推擠凹坑和裂縫,中間角度則混有前述兩種特徵。沖蝕率在沖擊角度30°以下時和硬度關係不大,將超過30°沖蝕率隨硬度同步增加,各回火條件試片的最大沖蝕率位在30~45°。 |
英文摘要 | The particle erosion behavior of SUS403 martensitic stainless steel tempered with five different temperatures range from 200°C to 600°C were studied as a function of impact angle and hardness. The results indicate that, the dominated mechanisms for material removal are cutting and extrusion at low and high impact angles, respectively. A transition of mechanism mixed by cutting and crater occurs at medium impact angle. Grain boundary cracking is often found for all impact angles that seem to be one of the major erosion mechanisms for two-phase materials mixed with martensite and ferrite. The erosion rate of all the experimental materials increases first, and then decreases with increase in impact angle. Thus, the maximum erosion rate occurred at the angle between 30° and 45°. At 15° and 30° of impingement, the erosion rate is virtually independent of hardness. While impact angles exceed than 30°, erosion rate increases with increasing hardness. |
本系統之摘要資訊系依該期刊論文摘要之資訊為主。