題 名 | 胺解聚酯纖維形態的SEM之研究=Study on the Morphology of the Aminolyzed Polyester Fibers by SEM |
---|---|
作 者 | 牟秀娟; 李陽世; | 書刊名 | 臺北科技大學學報 |
卷 期 | 33:1 2000.03[民89.03] |
頁 次 | 頁51-60 |
分類號 | 467.7 |
關鍵詞 | 聚酯織物; 胺解; 形態結構; Polyester fabrics; Aminolyzed; SEM; Morphology; |
語 文 | 中文(Chinese) |
中文摘要 | 使用七種不同胺類,分別以不同濃度、時間、溫度,處理聚醴織物,而使聚醴織 物產生胺解作用,導致纖維表面和芯心形態造成了改變,藉著SEM影像觀察和比較,並加以 探討纖維形態的側面微細變化,由結果顯示,經98%正丁基胺液胺解的聚醴織維具有光滑羊 毛鱗片狀之形態,使織物較具有輕柔之手感與光澤之觀感。 |
英文摘要 | Polyester fabrics were aminolyzed with seven kinds of aldylamines under varying conditions of concentration, treating time, and temperature. The degree of weight-reduction of the resulting fabrics was determined. The morphological variation of these aminolyzed fibers was observed using scanning electron microscope. The results show that the fabric treated with 98% n-butylamine aqueous solution had wool scale surface and exhibited silk-like handle. |