題名 | 對苯二甲酸/乙二醇/1,3丙二醇共聚合體在非等溫條件下結晶與裂解之探討=Non-Isothermal Crystallization and Degradation Behaviors of Terephalic Acid/Ethylene Glycol/1,3-propanediol Copolyesters |
---|---|
作者姓名(中文) | 石天威; 曾靖惠; | 書刊名 | 中華民國紡織工程學會誌 |
卷期 | 18:2 2000.11[民89.11] |
頁次 | 頁73-84 |
分類號 | 467.42 |
關鍵詞 | 聚酯共聚合體; 非等溫結晶; 熱裂解; Copolyester; Non-isothermal crystallization; Thermal degradation; |
語文 | 中文(Chinese) |
中文摘要 | 本篇主要在探討聚酯共聚合體非等溫結晶及其熱裂解行為。實驗所使用的共聚合體是以對苯二甲酸(Terephthalic acid,TPA),乙二醇(EthyleneGlycol)及1,3丙二醇(1,3-propanedio1,1,3-PD0)為共單體,合成不同比例之共聚合物,其中1,3丙二醇之莫耳體積分率為0-4。以微差掃描熱分析儀(Differential Scanning Calorimeter,DSC)及熱重分析儀 (Thermalgravimetric Analyzer,TGA),在不同的冷卻條件下,探討共聚合體之玻璃轉位溫度、結晶峰值溫度、熔融峰值溫度、裂解溫度、Ozawa指數m值及結晶速率常數k值。以Doyle-OzaWa積分法來計算裂解活化能。 結果發現,隨著1,3丙二醇含量增加,結晶峰值、熔融峰值及裂解溫度都有下降的趨勢。裂解活化能方面,在聚酯共聚合體中加入1,3丙二醇,將導致裂解活化能降低。Ozawa指數m值,指出不同比例的共聚合體皆呈現三維成長之球晶形態。 |
英文摘要 | The aim of the study was focused on non-isothermal crystallizationand thermal degradation behaviors of copolyesters, which weresynthesized by terephthalic acid / ethylene glycol / 1,3-propanediolwith varying copolymerization ratios. Here, the molar ratios of 1,3-propanediol is between 0∼4。 Glass transition temperature, crystallization peak temperatureTcp, melting peak temperature Tmp, degradation temperature Tdp,Ozawa exponent (m) and crystallization rate constant were studiedwith differential scanning calorimertry and thermal gravimetricanalyzer. The activation energy of non-isothermal degradation wascalculated by the Doyle-Ozawa integral method. The results show that Tcp, Tmp and Tdp decrease with an increaseof 1,3-propanediol content of copolyesters. The activation energiesof degradation decreased when the 1,3-propanediol was copolymerizedwith terephthalic acid/ ethylene glycol. Ozawa exponents indicatethat each of copolyesters has a 3-Dimention spherulitic structures. |