題名 | 含銅及鉛工業污泥水泥系固化體特性的初步研究=Initial Study on the Properties of the Cu and Pb Containing Industrial Sludge Cement-based Solidification |
---|---|
作者姓名(中文) | 薩支高; 黃世平; | 書刊名 | 國立屏東科技大學學報 |
卷期 | 6:4 1997.12[民86.12] |
頁次 | 頁283-291 |
分類號 | 445.2593 |
關鍵詞 | 含銅; 鉛污泥; 水泥系固化; |
語文 | 中文(Chinese) |
中文摘要 | 本研究的三種工業污泥材料均取自印刷電路板製造廠產生的電鍍廢水沉澱污泥, 分別編號為1號、2號及3號。三種污泥重金屬銅及鉛的全量均極高,其他如鋅、鎳及鉻含 量都較低,本實驗僅對污泥中銅及鉛兩種元素進行討論。經毒性特性溶出程序( TCLP )得 知三種污泥都是有害事業廢棄物。在 28 天內不同配比固化體單軸抗壓強度隨著養護時間的 延長而增大。 固化體之水泥╱污泥( C/S )比例越高則其抗壓強度越強,這是因為污泥是 含有高量重金屬之結構鬆散物,污泥量會影響水和水泥之間的水合反應而造成固化體的抗壓 強度降低。三種污泥固化體的抗壓強度並不相同,顯示污泥的性質確會影響固化試體的物理 性強度,特別是二號污泥中有機質含量較高,故所需的水泥需要量較高。添加飛灰可使污泥 固化體抗壓強度升高,在污泥所需適當的水泥添加量下添加飛灰,可減少水泥用量。重金屬 銅的溶出濃度依 C/S 比值增加而降低,鉛因溶出濃度低而並無變化, 此因鉛比銅較難被溶 出,污泥中鉛的含量較低也是影響溶出量不高的因素。 一般認為 C/S 配比愈高則固化效果 愈好,但 C/S 配比過大並不能線性減少 TCLP 溶出濃度。 |
英文摘要 | Three kinds of high Cu and Pb containing industrial sludge were selected as material in this study. From toxicity characteristic leaching procedure (TCLP), we know that all of the sludges are hazardous waste. Curing time elongation may increase the unconfined compressive strength of all solidified sludge samples with different cement to sludge (C/S) ratios. Higher C/S ratio may induce higher unconfined compressive strength too. Properties of sludge, especially organic matter content, were affect the pressure strength of solidified sludge. Fly ash addition was also proved to increase the unconfined compressive strength, which may be much help to fit the environmental standard. Higher C/S ratio were not linear decrease the TCLP results. Using unconfined compressive strength and TCLP can decide the most adequate C/S ratio of sludge solidification. However, it might increase the leaching amount of metals under the sludge base. Best C/S ratio is always the first step to prevent the secondly pollution. |