題 名 | Surface Changes and Bacterial Adhesion on Implant Abutment Materials after Various Clinical Cleaning Procedures |
---|---|
作 者 | Huang, Yu-shan; Hung, Cheng-yuan; Huang, Her-hsiung; | 書刊名 | Journal of the Chinese Medical Association |
卷 期 | 82:8 2019.08[民108.08] |
頁 次 | 頁643-650 |
分類號 | 416.96 |
關鍵詞 | Bacterial adhesion; Cleaning; Dental implant abutment; Titanium; Zirconia; |
語 文 | 英文(English) |
英文摘要 | Background: Supportive treatments are essential to long-term dental implant success; however, professional cleaning procedures may alter the surfaces of implant abutments and lead to adverse biological responses. This study aimed to evaluate four clinically used cleaning procedures by examining surface changes and subsequent bacterial adhesion on abutment materials. Methods: Discs of titanium and zirconia were polished and divided into five groups: titanium curette treatment, carbon fiber reinforced plastic curette treatment, ultrasonic scaling with carbon fiber tip treatment, air polishing with glycine powder, and control group without any treatment. After instrumentation, the arithmetical mean roughness (Ra), hydrophilicity, and surface free energy were recorded. The bacterial adhesion was evaluated after 1h of Streptococcus mitis incubation by optical microscope and quantified by turbidity test. Results: Among the titanium samples, titanium curette treatment group showed significant surface morphology changes, increased Ra, hydrophilicity, surface free energy, and higher optical density of adhered bacteria. As for the zirconia samples, the differences in surface morphology, Ra, and bacterial adhesion between groups were nonsignificant. Conclusion: Comparing to titanium, zirconia was less susceptible to surface changes after tested cleaning procedures. Titanium curette should be used with care on titanium abutments. |
本系統中英文摘要資訊取自各篇刊載內容。