| 題 名 | Effect of Temperature on the Properties of ZnO/Activated Carbon Composites from Spent Catalysts Containing Zinc Acetate |
|---|---|
| 作 者 | Zhang, Zhengyong; Niu, Hao; Fernández, Y.; Menéndez, J. A.; Peng, Jinhui; Zhang, Zebiao; Zhang, Libo; Duan, Xinhui; | 書刊名 | Journal of the Taiwan Institute of Chemical Engineers |
| 卷 期 | 41:5 2010.09[民99.09] |
| 頁 次 | 頁617-621 |
| 分類號 | 460.04 |
| 關鍵詞 | Spent catalyst; ZnO/activated carbon composites; Pore structure; Microstructure; |
| 語 文 | 英文(English) |
| 英文摘要 | Abstract After being subjected to conventional thermal treatment, a carbon-based spent catalyst from vinyl acetate synthesis has been proved to be a good precursor for the production of ZnO/activated carbon composites. Such composites can be used as photocatalysts for the removal of pollutants from wastewaters. Different operating temperatures were found to influence the properties of the final composites. As the temperature rises, the surface area of the activated carbon that is acting as catalyst support increases due to the decomposition of the organic deposits that are blocking the porous structure. XRD was used to evaluate the transformation of zinc acetate to zinc oxide after thermal treatment, showing higher crystal sizes with the rise in temperature. Both the adsorption capacity and the yield of the resulting composites were calculated and SEM-EDX analysis was used to evaluate the changes in surface morphology. |
本系統中英文摘要資訊取自各篇刊載內容。