| 題 名 | Manufacture and Mechanical Properties of Nanocomposite Laminates |
|---|---|
| 作 者 | Jen,R. Ming-hwa; Tseng,Yu-chung; Wu,Chun-hsien; | 書刊名 | 淡江理工學刊 |
| 卷 期 | 7:3 2004.09[民93.09] |
| 頁 次 | 頁167-170 |
| 分類號 | 440.34 |
| 關鍵詞 | Nanoparticles; Composite; Laminate; Mechanical property; Tensile test; |
| 語 文 | 英文(English) |
| 英文摘要 | This work mainly aims to manufacture nanocomposite laminates at first. The prepreg AS-4 graphite/PolyEtherEtherKetone laminates were used to make a 16-layered APC-2 laminate of 2 mm thick via curing the modified diaphragm. The nanoparticles of Silica (SiO2) were uniformly spread on the specific interfaces totally about 1-3% by weight of a laminate by sol-gel method. second, by the results of mechanical testing we fond that the optimal content of nanopearticles is 1% of weight percentage, and the ultimate strength increases with 10% and the corresponding stiffness increases with 22% in the quasi-isotropic nanocomposite laminates. At elevated temperature, the ultimate strength and the stiffness of the mechanical properties drop slightly below 75℃, and degrade highly at 150℃ |
本系統中英文摘要資訊取自各篇刊載內容。