查詢結果分析
來源資料
相關文獻
- Novel Method to Prepare Conductive Coatings from Metal Chelate of Polyester
- Influences of Adding LiCF[feb0]SO[feb0]-PC on the Conductivity of H[feba]MDI Based WPU Electrolytes
- The Preparation and Property Study on Metallized Nylon4 Films
- 牛乳導電度檢測門檻值決定之研究
- 金屬材料塗佈織物抗靜電之研究
- 椰纖集合體用於無土栽培上的研究
- 馬桶尿液殘留測試--導電度法之建立
- Novel Waterborne Polyurethane Based Electrolyter for Lithium Batteries(Ⅳ)--The Influence of DMPA/PEG Ratios on Conductivity
- 普通化學中的固態化學實驗設計
- 表面聲波感測器液體負載特性量測
頁籤選單縮合
題 名 | Novel Method to Prepare Conductive Coatings from Metal Chelate of Polyester=聚酯金屬螯物導電性塗料之新穎製備法 |
---|---|
作 者 | 黃鵲容; 劉宗宏; | 書刊名 | 修平學報 |
卷 期 | 1 2000.09[民89.09] |
頁 次 | 頁85-96 |
分類號 | 465.66 |
關鍵詞 | 導電塗料; 聚醋酸乙烯酯; 表面電阻; 導電度; Conductivity coating; Metal chelate; Polyvinyl acetate; Surface resistivity; |
語 文 | 英文(English) |
中文摘要 | 本研究開發一系列新型之聚醋酸乙烯酯金屬螯物導電塗料,並研究此型塗料之導 電性質與製造方法。 本研究利用具黏著性質的聚醋酸乙烯酯聚合體和過渡金屬鹽類( AgNO �陛ACaCl �砥A NiCl �祟M CoCl �秘央^製成聚醋酸乙烯酯金屬螯合溶液, 將此溶液塗佈在 PET 的基板上,經過乾燥及硼氫化鈉的還原後,基板上塗層的表面電阻可達到 1 �� /cm �� 以下。還原後之塗層經由 SEM 和 X-ray 之分析數據,確定塗層表面有金屬之形成,這層均 勻的金屬層是塗料具有優良導電度的原因。本研究並利用 FTIR 光譜分析和黏度分析來測定 螯合物的生成結構。本研究方法所製成的金屬螯物塗料除了導電性優異外,對基材亦有良好 的黏著性。 |
英文摘要 | The conductive polyvinyl acetate (PVAc) chelate coatings were prepared by spreading various mixtures of transition-metal salts (AgNO ��,CuCl ��,NiCl �� and CoCl �� ) and polyvinyl acetate in formic acid solution onto PET sheet substrates and dried by heat treatment and reduced with sodium borohydride aqueous solution, which were found to have surface resistivity less than 1 �� /cm ��. The IR spectra and the viscosity of the metal chelate mixtures, as well as the SEM of the coating surfaces before and after reduction were studied. The PVAc-metal chelate coatings not only had good adhesion to the substrates, but also exhibited stable and excellent conductivity. And by means of X-ray diffraction analysis, these reduced coatings were shown to have metallized surfaces that were believed to be responsible for the excellent conductivity. |